What is the shape factor for a cylinder in terms of powdered materials used in the sintering process?
Wiki User
∙ 11y ago
The general form for the shape factor of any shape is:
Ks = (DeA) / V
where
Ks : Shape Factor
De : Equivalent Diameter of a sphere with a volume equal to the volume of the non-spherical particle
A : Area of the shape
V : Volume of the shape
By setting the equation for the volume of a sphere and the volume of the shape in question (in this case a cylinder) we can find De.
De = ((3/4) r2 h)(1/3)
De : Equivalent Diameter
D : Diameter of the cylinder
h : height of cylinder
Substituting the formula for the area and volume of a cylinder and the De into the general form will give us the shape factor for a cylinder.
Wiki User
∙ 11y ago
Add your answer:
Earn +20 pts
What is the bonding process for powdered metals?
The process is called sintering and is based on atoms diffusion.
Sintering of carbides?
Sintering is a process where powdered carbide materials are heated below their melting point to create strong bonds between particles, resulting in a denser final product with improved mechanical properties. This technique is commonly used in the manufacturing of cutting tools, wear-resistant parts, and other high-performance applications.
What is the difference between sintering and annealing?
Sintering is a process of compacting and forming a solid mass of material using heat without reaching its melting point, while annealing is a heat treatment process that involves heating a material to a specific temperature and then slowly cooling it to relieve internal stresses and increase ductility. Sintering is used to form objects, while annealing is used to improve a material's properties.
What is meant by selective laser sintering?
Selective laser sintering is the process of using an additive in a manufacturing technique that uses an ultra high powered laser and is used for prototype models and functional components.
What has the author Udom Techakijkajorn written?
Udom Techakijkajorn has written: 'Sintering of fume deposits in kraft recovery boilers' -- subject(s): Fume control, Sintering, Sulphate pulping process, Paper industry
What is sinter?
Sintering is a process used when manufacturing ceramic or steel objects. The method of sintering is when objects are made from small particles being heated in a furnace below their solid state, which cause the particles to weld to each other.
What is the difference between calcination temperature and sintering temp?
Calcination temperature is the temperature at which a material is heated to remove volatile components and initiate a chemical reaction, while sintering temperature is the temperature at which particles in a compacted material bond together to form a solid piece. Calcination typically occurs at lower temperatures than sintering.
What is the furnace method?
The furnace method refers to a process where materials are heated in a furnace to high temperatures for purposes like melting, sintering, or calcining. This method is commonly used in industries such as metalworking, ceramics, and glass manufacturing.
Is graphite a ceramic material?
No, graphite is not a ceramic material. Graphite is a form of carbon with a layered structure, while ceramics are non-metallic materials made through the process of firing, sintering, or other methods.
What is the process when powdered limestone reacts with the acid in the lake?
o
What is pressure sintering in ice?
Pressure sintering in ice is a process where pressure is applied to powdered ice at low temperatures, causing the particles to bond together and form a solid object without melting. This method helps to create dense and strong ice structures with controlled porosity and improved mechanical properties.
What is binder burnout and sintering?
In ceramic processing, polymers are often added to ceramic particles to allow for higher densities and sufficient green strength. The green body, or pre-fired ceramic, must have sufficient strength to hold its shape after being pressed. Binder burnout is a processing step performed before sintering, where the green body is heated until the polymer binder is burned out of the ceramic. Sintering is the process by which ceramics are densified. Sintering is done because ceramics have very high melting temperatures and reactive melts. In sintering, the green ceramic is heated to a high temperature, below the melting point of the ceramic, where high rates of diffusion are possible. The ceramic particles are joined into a solid monolith through diffusional movement of atoms.